"Biodegradación de polietileno mediante el uso de microorganismos"
Authors
Loading...
Date
2020
Directors
Journal Title
Journal ISSN
Volume Title
Publisher
Quevedo-UTEQ
Abstract
El polietileno es un polímero que causa grandes problemas ambientales a nivel mundial,
debido a su composición a base de hidrocarburos le brinda propiedades únicas de durabilidad
en la naturaleza lo que impide que la misma lo degrade, de este modo se vuelve un agente
toxico en el ecosistema; los microorganismo ofrecen una solución viable en la
descomposición del polietileno lo que nos lleva a la búsqueda de conocer que mecanismos
utilizan para lograr dicho fin por lo que se vuelve una alternativa viable para degradar dicho
polímero.
Para el presente trabajo se escogió diferentes cepas del laboratorio de biología molecular y
microbiología de la UTEQ;. Se realizaron pruebas bioquímicas (degradación de urea, fósforo
y potasio), se midió la absorbancia, biomasa, UFC, pH, degradación de polietileno y se
correlacionó la absorbancia con las UFC. Entre los resultados, la mayor absorbancia tuvo
la cepa VI8 a los 0.21 a los 10 días, la cepa bacteriana que generó mayor biomasa celular
fue RR4 generó promedios de 0.06 gr/ml a los 10 días, el contenido celular de las bacterias
en el VI8 alcanzó promedios de 2.1𝑥10
6
, el Potencial de Hidrogeno en la cepa PN7 se
mantuvo un pH de 7.2 a 6.6 durante los 30 días, en la degradación de polietileno, la cepa con
mayor degradación de polietileno a 300 mg fue la cepa VI8 redujo de 32 y 38 mg a los 15 y
30 días respectivamente. Se concluyó que la velocidad en la degradación depende de
múltiples factores bioquímicos como la producción de ácidos orgánicos e inorgánicos que
desdoblan las moléculas del plástico en fracciones más sencillas que pueden ser asimiladas
por otro tipo de microorganismos.
Palabras clave: Contaminación, O.D. Preservación, Ureasa, Fosfatasa
Description
Polyethylene is a polymer that causes global environmental problems through degradation
and deterioration that leads to its accumulation in the environment and, therefore, creates
serious environmental problems. An attempt has been made to cover the biodegradation
mechanism, the various bacterial and fungal organisms that have been reported for them, the
methods adopted for the studies and the different characterization techniques followed to
measure the degree of degradation. Different strains from the UTEQ molecular biology and
microbiology laboratory were chosen for the respective work. Biochemical tests were
performed (degradation of urea, phosphorus and potassium), absorbance, biomass, CFU, pH,
polyethylene degradation were measured and absorbance was correlated with CFU. Among
the results, the VI8 strain had the highest absorbance at 0.21 at 10 days, the bacterial strain
that generated the highest cell biomass was RR4, which generated averages of 0.06 gr / ml
at 10 days, the cell content of bacteria in VI8 reach averages of 2.1x10 ^ 6, the Hydrogen
Potential in the PN7 strain was maintained at a pH of 7.2 to 6.6 during the 30 days, in the
degradation of polyethylene, the strain with the greatest degradation of polyethylene at 300
mg was the strain VI8 reduced 32 and 38 mg at 15 and 30 days respectively. It was concluded
that the rate of degradation depends on multiple biochemical factors such as the production
of organic and inorganic acids that break down the plastic molecules into simpler fractions
that can be assimilated by other types of microorganisms.
Keywords: Contamination, D.O. Preservation, Urease, Phosphatase
Keywords
Contaminación, O.D. preservación, Ureasa, fosfatasa
Citation
Vargas Cedeño.Gissela Eloisa. (2020). "Biodegradación de polietileno mediante el uso de microorganismos". Quevedo. UTEQ. 53 p.